Quim. Nova, Vol. 36, No. 6, 762-767, 2013

Artigo

SÍNTESE E CARACTERIZAÇÃO DE CaZrO3 E BaZrO3 NANOESTRUTURADOS
Amanda Laura Ibiapino e Laysa Pires de Figueiredo
Departamento de Química, Instituto de Ciências Exatas e da Terra, Universidade Federal do Mato Grosso, 78060-900 Cuiabá-MT,
Brasil
Gustavo E. Lascalea
LISAMEN/CONICET, Av. Dr. Ruiz Leal s/n, Parque Gral. San Martín, Ciudad de Mendoza, 5500, Argentina
Rogério Junqueira Prado*
Instituto de Física, Universidade Federal do Mato Grosso, 78060-900 Cuiabá - MT, Brasil
Recebido em 26/4/12; aceito em 17/12/12, publicado na web em 28/3/13

SYNTHESIS AND CHARACTERIZATION OF NANOSTRUCTURED CaZrO3 AND BaZrO3. In this work, nanostructured samples of barium zirconate (BaZrO3) and calcium zirconate (CaZrO3) were synthesized by the gel-combustion method, using glycine as fuel.
The ceramic powders were calcined at 550 °C for 2 h and subsequently heat treated at 1350 °C for 10 min (fast-firing). The X-ray diffraction technique was employed to identify and characterize the crystalline phases present in the synthesized powders, using the
Rietveld method. Monophasic nanostructured samples of BaZrO3 and CaZrO3 presenting average crystallite sizes of around 8.5 and
10.3 nm, respectively, were found after fast-firing.
Keywords: nanostructured materials; Rietveld method; gel-combustion method.

INTRODUÇÃO
A nanociência e a nanotecnologia figuram como áreas das mais atraentes e promissoras para o desenvolvimento científico e tecnológico do século XXI. Na literatura científica são encontrados diversos termos a elas relacionados, dentre os quais se destacam nanopartículas, nanocristais, nanofios, nanofitas, nanotubos e nanocompósitos.1