FACULDADE DE ENGENHARIA DA UNIVERSIDADE DO PORTO Departamento de Engenharia Mecânica e Gestão Industrial

Estudo da estrutura e comportamento tribológico de revestimentos duros e ultra-duros executados no vácuo
Francisco José Gomes da Silva

Mestre em Engenharia Mecânica pela Faculdade de Engenharia da Universidade do Porto

Dissertação submetida para a obtenção do grau de doutor emEngenharia Mecânica

Dissertação realizada sob a supervisão de Professor Doutor António Paulo Monteiro Baptista do Departamento de Engenharia Mecânica e Gestão Industrial da Faculdade de Engenharia da Universidade do Porto e Professora Doutora Maria Estela M. F. Pereira do Departamento de Física da Universidade de Aveiro

Porto, Novembro de 2001

Resumo

3

RESUMO

Os revestimentos durostêm assumido uma importância crescente em aplicações tribológicas. O diamante, devido à sua elevada dureza e condutividade térmica, tem sido alvo de muitas investigações com vista a esse tipo de aplicações. No entanto, devido à elevada instabilidade do C na presença do Fe, os revestimentos a diamante de substratos de aço nunca conheceram sucessos significativos. Este trabalho pretendeu encontrar asmelhores condições de síntese de diamante em substratos ferrosos, procedendo seguidamente a testes tribológicos de avaliação das eventuais vantagens fornecidas por este tipo de revestimento. A síntese do diamante foi efectuada por MPCVD (Microwave Plasma Chemical Vapour Deposition). A sua morfologia e qualidade foram avaliadas por Microscopia Electrónica de Varrimento (MEV / SEM), Rugosimetria eEspectroscopia Raman. Os testes tribológicos foram realizados num equipamento de micro-abrasão e a avaliação do desgaste foi analisada por Microscopia Óptica, Microscopia Electrónica de Varrimento (MEV / SEM + EDS) e Rugosimetria.

Revestimentos duros e ultra-duros executados no vácuo

Novembro de 2001

Abstract

4

ABSTRACT
Hard coatings have been assuming an important rule intribological applications. Diamond coatings are very attractive for many of these applications and they are subject of an intensive investigation. However, due to the catalytic effect of Fe and large carbon solubility in it, diamond coatings on ferrous substrates never met significant successes. To find the best conditions for diamond synthesis in ferrous substrates was the goal of this work. Afterwards,tribological tests were performed to investigate the eventual advantages of these coatings. The synthesis of the diamond was conducted by MPCVD (microwave plasma chemical vapour deposition). Morphology, quality and stress were evaluated by scanning electron microscopy (SEM), profilometry and Raman spectroscopy. Tribological tests were accomplished in micro-abrasion equipment and the wearevaluation was analysed by optical microscopy, scanning electron microscopy (SEM + EDS) and profilometry.

Revestimentos duros e ultra-duros executados no vácuo

Novembro de 2001

Résumé

5

RÉSUMÉ

Les revêtements durs ont assumé un rôle très important dans les applications tribologiques. Les revêtements au diamant sont très intéressants pour beaucoup de ces applications et ils sont soumis àdes études intensives. Cependant, dû à l'effet catalytique du Fe et à la grande solubilité du carbone dans ce métal, les couches de diamant sur des substrats ferreux n'ont jamais rencontré des succès considérables. Trouver les meilleures conditions pour la synthèse du diamant sur des substrats ferreux était le but de ce travail. Ensuite, ont à exécuté des essais tribologiques pour enquêter sur leséventuels avantages de ces revêtements. La synthèse du diamant a été conduite par MPCVD (microwave plasma chemical vapour deposition). La morphologie, la qualité et le niveau de contraintes résiduelles ont été évalués par microscopie électronique à balayage (SEM), par rugosimetrie et par spectroscopie Raman. Les essais tribologiques ont été réalisés en utilisant une machine de micro-abrasion...