Zylar® 960
Clear Impact Modified Acrylic Copolymer DRAFT PRODUCT DATA SHEET

• Outstanding practical toughness • Excellent clarity • Custom colors available • FDA compliant • USP XXIII Class VI Approved • UL 94 HB @1.5 mm all colors, (www.UL.com file E55776) • Bisphenol A and phthalate free

• Medical devices • Housewares

PRODUCT • Cosmeticpackaging
• Floor care and appliances • Point-of-purchase displays • Pens and pencils • Toys and consumer goods


Properties of

English Typical (2) Values
6 590 NB 19 23 1,720 70 43 1,720 94 86 62

Melt Flow Rate, 200/5.0 Impact Strength, Notched Izod Impact Strength, Unnotched Izod Impact Strength, Gardner Tensile Strength, Yield Tensile Modulus Elongation,Break Flexural Strength, Break Flexural Modulus Vicat Softening Temp. Heat Deflection Temp. Hardness, Rockwell Mold Shrinkage Water Absorption (24 hr) Haze Specific Gravity
(1) (2) (3)


g/10 min J/m J MPa MPa % MPa MPa ° C ° C R scale mm/mm % % -

g/10 min ft-lb/in In/lb psi psi x 10 % psi psi x 10 ° F ° F R scale in/in % % 3 3

Typical (2) Values
6 11 NB 170 3,400 250 706,200 250 201 187 62 0.002 – 0.006 0.1 2 1.05



D 1238 D 256 D 5420 D 638 D 638 D 638 D 790 D 790 D 1525 D 648 D 785 D 955 D 570 D 1003 D 792

0.002 – 0.006 0.1 2 1.05

Colored material may differ in some properties. Typical Values represent average laboratory values and are intended as guides only, not as specific specification limits. All molded samples were 1/8-inch (3.2 mm)thick unless noted. HDT/DTUL properties measured on annealed bars.

Styrolution 25846 SW Frontage Road | Channahon, IL 60410 | Phone +1.815.423.5541 or +1.866.890.6353 | Fax +1.866.890.6362 www.styrolution.com | www.zylar.com | E-mail info_north_america@styrolution.com

Page 1 of 2

The above information is provided in good faith. Styrolution is not responsible for any processing orcompounding which may occur to product finished articles, packaging materials or their components. Further, Styrolution MAKES NO WARRANTY OR REPRESENTATION OF ANY KIND, REGARDING THE INFORMATION GIVEN OR THE PRODUCTS DESCRIBED, AND EXPRESSLY DISCLAIMS ALL IMPLIED WARRANTIES, REPRESENTATIONS AND CONDITIONS, INCLUDING WITHOUT LIMITATION ALL WARRANTIES AND CONDITIONS OF QUALITY, MERCHANTABILITY ANDSUITABILITY OR FITNESS FOR A PARTICULAR PURPOSE. Responsibility for use, storage, handling and disposal of the products described herein is that of the purchaser or end user.

Zylar® 960
Clear Impact Modified Acrylic Copolymer DRAFT PRODUCT DATA SHEET

TEST METHODS The product properties designated in this standard have been determined in accordance with the current issues of thespecified testing methods. Methods of the American Society for Testing and Materials (ASTM) are used wherever applicable. PROCESSING
Injection Molding(1)
Melt Temperature

PRE-DRY REQUIREMENTS Zylar 960 is a low moisture absorption copolymer and, in many instances, processes readily without pre-drying. There are PRODUCT DATA the product be combinations of conditions that require thatSHEETdried, such as high humidity and heavy section molding. Two (2) hours at 150ºF (65ºC) is adequate for most applications. Dehumidifying type dryers are recommended. MOLD REQUIREMENTS To obtain maximum clarity and gloss from this product it is necessary to have a highly polished mold. Design of gates, runners and sprues can be patterned after standard practice for high-heat polystyrene. All mold surfacesmust be temperature controlled at 130ºF (54ºC) for optimum clarity and surface gloss. MACHINE PREPARATION For optimum clarity, machine cylinders, barrels, screws, valves, etc., should be thoroughly cleaned before processing. Contamination by other materials will cause streaking or haze. AVAILABILITY Styrolution resins are available in bulk railcar and truckload quantities, multiwall bags or...